焊丝牌号 | 焊丝编号 | GB | AWS | 其它标准 | 焊丝直径(mm) | 焊丝分类 | 焊接方法 | 保护气体 | C(%) | Si(%) | Mn(%) | S(%) | P(%) | Mo(%) | Cr(%) | Ni(%) | V(%) | Ti(%) | Al(%) | Cu(%) | Fe(%) | 其它(%) | σb(MPa) | σs(MPa) | δ5(%) | 冲击温度(℃) | Akv(J) | 备注 | 数据来源 |
H08MnMoA | S10000 | * | * | * | 4.0 | * | 埋弧焊 | * | 0.082 | 0.19 | 1.48 | 0.014 | 0.018 | 0.39 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * |
H10MnMo | S10001 | * | * | * | 3.0 | * | 电渣焊 | * | 0.102 | 0.24 | 1.50 | 0.018 | 0.022 | 0.40 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * |
H08MnMoA | S10002 | * | * | * | 5.0 | 合金结构钢 | 埋弧焊 | * | 0.040 | 0.11 | 1.64 | 0.008 | 0.012 | 0.40 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | 哈焊所数据 |
H08MnMoA | S10003 | * | * | * | 5.0 | 合金结构钢 | 埋弧焊 | * | 0.060 | 0.18 | 1.16 | 0.017 | 0.017 | 0.50 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | 九江桥焊接试验组数据 |
H08CrMoSi | S10004 | * | * | * | 2.0 | 合金结构钢 | 氩弧焊 | Ar | 0.050~0.050 | 0.78 ~0.78 | 1.57 ~1.57 | 0.008~0.008 | 0.012~0.012 | 0.42 ~0.42 | 0.91 ~0.91 | * | * | * | * | * | * | * | * | * | * | * | * | * | 哈尔滨焊接研究所 |
H10MnSi | * | * | * | Q/DQ-P29-001-87 | 2.0 | 合金结构钢 | 氩弧焊 | Ar | * | 0.65 ~0.95 | 0.80 ~1.00 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * |
H10MnSi | S10005 | * | * | * | 2.0 | 合金结构钢 | 氩弧焊 | Ar | 0.090~0.090 | 0.77 ~0.77 | 0.92 ~0.92 | 0.010~0.010 | 0.012~0.012 | * | 0.023~0.023 | 0.020~0.020 | * | * | * | * | * | * | * | * | * | * | * | * | 哈尔滨焊接研究所 |
H1Cr18Ni9Ti | S10006 | * | * | * | 2.0 | 不锈钢 | 氩弧焊 | Ar | 0.060~0.060 | 0.53 ~0.53 | 1.20 ~1.20 | 0.003~0.003 | 0.028~0.028 | * | 17.49~17.49 | 9.06 ~9.06 | * | 0.56 ~0.56 | * | * | * | * | * | * | * | * | * | * | 哈尔滨焊接研究所 |
H1Cr18Ni9Ti | * | * | * | Q/DQ-P29-001-87 | 2.0 | 不锈钢 | 氩弧焊 | Ar | * | 0.30 ~0.70 | 1.00 ~2.00 | * | * | * | 18.00~20.00 | 8.00 ~10.00 | * | 0.50 ~0.80 | * | * | * | * | * | * | * | * | * | * | * |
H08Mo2Si | S10007 | * | * | * | 3.0 | 合金结构钢 | 氩弧焊 | CO2 | 0.099 | 0.89 | 2.02 | 0.012 | 0.015 | * | * | * | * | * | * | * | * | * | * | * | * | * | * | * | 哈尔滨焊接研究所 |
|